Water sorption and bond strength of graphene oxide-added universal adhesives
BMC Oral Health, cilt.26, sa.1, 2026 (SCI-Expanded, Scopus)
- Yayın Türü: Makale / Tam Makale
- Cilt numarası: 26 Sayı: 1
- Basım Tarihi: 2026
- Doi Numarası: 10.1186/s12903-026-08360-0
- Dergi Adı: BMC Oral Health
- Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus, CINAHL, EMBASE, MEDLINE, Directory of Open Access Journals, Natural Science Collection (ProQuest), Biological Science Database (ProQuest), Biomedical Reference Collection: Corporate Edition (EBSCO), Health Research Premium Collection (ProQuest)
- Anahtar Kelimeler: Adhesion, Dentin, Durability, Graphene oxide, HEMA, Water sorption
- Süleyman Demirel Üniversitesi Adresli: Evet
Özet
Objective: To evaluate the effect of adding graphene oxide (GO) to HEMA-containing and HEMA-free universal adhesives on water sorption/solubility and bonding effectiveness to dentin. Materials and methods: GO was incorporated into universal adhesives (Scotchbond Universal and G-Premio Bond) at three weight percentages (0.5, 1, and 3%) and characterized by SEM. Clearfil SE Bond was used as the reference adhesive. Disk-shaped specimens were prepared to evaluate water sorption and solubility (n = 10). Microspecimens were prepared from ninety extracted human third molar. The µTBS of half of the specimens was tested after 24 h, and the remaining specimens were aged for 6 months. Failure mode was analyzed using a stereomicroscope. Statistical analyses were performed with one-way ANOVA, Duncan, and paired t-tests (p = 0.05). Results: Adding 3% GO increased water sorption of the adhesives (p < 0.05). Clearfil SE Bond exhibited the lowest water sorption and solubility (p < 0.05). 1% GO significantly increased the immediate µTBS of the adhesives, whereas 3% resulted in a significant decrease (p < 0.05). 0.5 and 1% GO significantly increased the aged µTBS of Scotchbond Universal, while only 1% improved the aged µTBS of G-Premio Bond (p < 0.05). 3% GO reduced the aged µTBS of the adhesives (p < 0.05). The highest immediate and aged µTBS were recorded for Clearfil SE Bond (p < 0.05). Conclusions: The bonding performance of universal adhesives improved with 0.5% and 1% GO additions, whereas 3% GO had a detrimental effect on both bond strength and water sorption. Clinical significance: Adding GO to adhesives may improve the long-term durability of bonded restorations.